Fiber Optic Cable |
Cable Cross Section |
|
| x is Number of Cores & x<=36 |
|
Loose Tube Fiber Optic Cable |
SM, 2~36C,
Fig.8
Self-Supporting,
Single Jacket |
 |
Application :
Aerial |
| |
|
If
Number of cores will be 36<x≤96
then:
1. Messenger wire change to 7x1.2
mm
2. Number of fiber/ tube will be change |
|
|
Cable Construction & Description
|
| |
|
| Fiber
Coloring : |
UV Curable Acrylic Color
Ink |
| No.
of Tube : |
Max. 6Tubes |
| No.
of fiber/Tube : |
Max. 6 Fibers |
| Loose
Tube Material : |
PBT |
| Filling
compound (Tube) : |
Thixotropic Jelly |
|
Central Strength Member : |
FRP (Nom. 2.3mm Dia.) |
| Water
Blocking (Core) : |
Water Swell Jelly |
| Core
Wrap : |
Water Swell able Tape |
|
Messenger Wire : |
Gal. Steel Wire(0.8mm*19wires) |
| Outer
Sheath (Figure-8) : |
Black MDPE |
|
Cable Core : |
Nom. 2.0mm Thick. |
|
Web Size : |
(0.3W x 4.0H) ± 0.5mm |
|
Messenger Wire : |
Nom. 1.5mm Thick. |
| Cable
Marking : |
Cable type, Fiber Counts |
|
Name of Manufacturer |
|
Year of Manufacturing, |
|
Cable Length in meter |
| Cable
Outside Diameter : |
Nom. 22.3 / 11.3mm |
| Cable
Weight : |
Approx. 270kg/km |
| Packing
: |
Export Wooden Drum |
|
Bending Radius : |
Static: 10D (Diameter of cable) |
| |
Dynamic: 20D (Diameter of cable) |
| |
|
Optical Fiber Performance |
| |
| 1.Optical
& Geometrical Performance |
| |
|
|
| |
Mode Field Diameter
: |
9.2 ± 0.4 μm at 1310 nm |
| |
Mode Field Concentricity
Error : |
≤ 0.8μm |
| |
Cladding Diameter : |
125 ± 1μm |
| |
Cladding Non-Circularity: |
≤ 1% |
| |
Coating Diameter : |
245 ± 10μm |
| |
Coating Non-Circularity
Error : |
≤ 6% |
| |
Attenuation Coefficient
: |
≤ 0.36dB/km at 1310nm |
| |
|
≤ 0.22dB/km at 1550nm |
| |
Chromatic Dispersion
: |
≤3.5ps/nm/km at1285~1330nm |
| |
|
≤18ps/nm/km at 1550nm |
| |
Cut-off Wavelength
(λcc) : |
≤ 1260nm |
| |
Zero Dispersion Wavelength
: |
1300~1322nm |
| |
PMD Coefficient : |
≤ 0.2ps/√km |
| |
Point Discontinuity
: |
≤ 0.05 dB at 1310 & 1550nm |
| |
Effective Group Index
of : |
1.4677 at 1310nm(Typical) |
| |
Refraction (Neff) : |
1.4682 at 1550nm(Typical) |
| |
Type of Fiber Core : |
MCSM |
| |
| 2.Mechanical
& Environmental Performance |
| |
| |
Proof Test Level : |
≥ 0.69 GPa(≥100kpsi) |
| |
Macro bending : |
≤ 0.05 dB at 1550nm |
| |
(at 75mm dia. x100 turns) |
| |
Temperature Dependence
: |
≤ 0.05 dB/km at 1550nm |
| |
(-60°C to 85°C) |
| |
Damp Dependence: |
≤ 0.05 dB/km at 1550nm |
| |
(+80°C,85%RH for 30Days) |
| |
Water soak Dependence
: |
≤ 0.05 dB/km at 1550nm |
| |
(+20°C for 30Days) |
| |
|
Identification of optical fiber & Loose Tube |
| |
|
Optical Fiber |
Loose Tube |
|
1 |
Blue |
1 |
Blue |
|
2 |
Orange |
2 |
Orange |
|
3 |
Green |
3 |
Green |
|
4 |
Brown |
4 |
Brown |
|
5 |
Grey |
5 |
Grey |
|
6 |
White |
6 |
White |
|
| |
|
Mechanical & Environmental Performance |
| |
|
Item |
Reference |
Test
Condition |
Acceptance Criteria |
|
Tensile Strength |
IEC 794-1-E1 |
Long Term : 1000N,
Short Term : 3000N |
Attenuation Increase : ≤0.05dB |
|
Crush |
IEC 794-1-E3 |
Loading : 5000N/100mm |
Attenuation Increase : ≤0.05dB |
|
Impact |
IEC 794-1-E4 |
Loading : 10N.m,
Cycle : 5 |
Attenuation Increase : ≤0.05dB |
|
Repeated Bend |
IEC 794-1-E6 |
Bending Radius : X 20D,
Cycle : 30 |
Attenuation Increase : ≤0.05dB |
|
Torsion |
IEC 794-1-E7 |
Length : 1m,
Torsion angle : ±180,
Cycle:10 |
Attenuation Increase : ≤0.05dB |
|
Cable Bend |
IEC 794-1-E11 |
Bending Radius : X 10D,
Cycle : 10,
Turns : 5 |
Attenuation Increase : ≤0.05dB |
|
Temp. Cycling |
IEC 794-1-F1 |
Step :+20°C->-40°C°C-
>+70°C->+20°C, 24Hrs |
Attenuation Increase : ≤0.1dB/km |
|
Water Penetration |
IEC 794-1-F5 |
Length : 1m,
Height : 1m,
Times : 24Hrs |
No Leakage |
|
| |